Importance Factor for Synthesis Original Compound (Na,K)2CO3 of New Type BLSF Lead-Free Ceramics (Na,K)2Bi6Ti7O24

Tai Kuang Lee, Wen Hsi Lee

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

New type BLSF ceramics (Na,K)2Bi6Ti7O24 (NKBT) were safely and environmental protection lead-free material. The dielectric constant of 30, and tanδ=2.3%.This study manufactured original compound material (Na,K)2CO3 of NKBT, successfully. New type BLSF ceramics NKBT were yet produced a successfulin the past. After a series of efficient and accurate results showed keys of successfully producing NKBT is synthesis of sodium carbonate and potassium carbonate prior to original compound-(Na,K)2CO3. Chloride anion(Cl-) in water, shear force by mixing and drying temperature are the keys to a successful factor. In this paper, we get optimal (Na,K)2CO3 powder by rotation velocity 300 rpm and drying temperature 110°C. (Na,K)2CO3 powder had the advantageof uneasy deliquesce, manufacturing process easy,fast and low working temperature because of using integration and synthesis of carbonic oxide and there was clear evidence of (Na,K)2CO3 by scientific instruments as Scanning Electron Microscope (SEM) etc.

原文English
頁(從 - 到)956-965
頁數10
期刊Chinese Journal of Physics
50
發行號6
出版狀態Published - 2012 十二月

All Science Journal Classification (ASJC) codes

  • 物理與天文學 (全部)

指紋

深入研究「Importance Factor for Synthesis Original Compound (Na,K)<sub>2</sub>CO<sub>3</sub> of New Type BLSF Lead-Free Ceramics (Na,K)<sub>2</sub>Bi<sub>6</sub>Ti<sub>7</sub>O<sub>24</sub>」主題。共同形成了獨特的指紋。

引用此