Improve subsequent leaching efficiency and extraction rate of germanium in optical fibre cables with pre-treatment

Wei Sheng Chen, Bi Cheng Chang, Chih Kang Shuai

研究成果: Conference article

摘要

Germanium is an important and rare material which widely used in fibre optic industry, accounting for about 40% of the total germanium product usage. Due to the rarity of germanium, developing an effective recycling process of recovering germanium metal from waste fibre optical cables is significant. Fibre optical cables was arranged to do characteristic analysis, pre-treatment and dissolution in this study. In the characteristic analysis, the content of germanium dioxide in the glass fibre was 0.15%, and the remaining components were all silicon dioxide. In the pre-treatment part, it consists of two steps which are the solvent treatment and roasting. At the solvent treatment step, glass fibre can be separated by acetone with a concentration of more than 50% and ethanol with concentration of more than 75%. At the roasting step, NaOH was used as a roasting additive. Adding 5 molar ratio of NaOH/SiO2 at 500 °C for 2 hours can totally convert the optical fibre into the silicate. After roasting, it could be leaching by dilute H2SO4 and its leaching rate is higher than 99.5%. This study can provide a process to recovery germanium from optical fibre effectively. According to the optimal conditions, the recovery of germanium could be up to 99%.

原文English
文章編號012005
期刊IOP Conference Series: Materials Science and Engineering
720
發行號1
DOIs
出版狀態Published - 2020 一月 7
事件4th International Conference on Optics in Materials, Energy, and Technologies 2019, ICOMET 2019 - Tainan, Taiwan
持續時間: 2019 六月 242019 六月 28

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Engineering(all)

指紋 深入研究「Improve subsequent leaching efficiency and extraction rate of germanium in optical fibre cables with pre-treatment」主題。共同形成了獨特的指紋。

  • 引用此