In-situ and ex-situ comparison of oxidation of Inconel 718 manufactured by selective laser melting and conventional methods up to 650 °C

Maryam Beyhaghi, Mehdi Rouhani, Jonathan Hobley, Yeau Ren Jeng

研究成果: Article同行評審

15 引文 斯高帕斯(Scopus)

摘要

This work reveals the initial stages of Inconel 718 (IN718) oxidation manufactured by selective laser melting (SLM). In-situ and ex-situ investigations were conducted on SLM-IN718 and a commercially obtained Inconel 718 sample (Comm-IN718) to compare their oxidation behavior. In-situ and ex-situ testing was performed using a unique synchronized system integrating precise thermal control with Raman spectroscopy, optical microscopy and scanning probe techniques. X-Ray diffractometry (XRD) and Scanning Electron Microscopy (SEM) were used for microstructure analyses before and after heating. Raman spectroscopy indicated that, in both samples, there is a threshold temperature for oxidation at around 300 °C. The highest rate of oxidation was observed up to 550 °C as different oxides form. After 550 °C, there was no noticeable formation of new compounds up to 650 °C. Extended heating at 650 °C resulted in further changes in the Comm-IN718 sample, however the SLM-IN718 sample was unchanged by longer heating times. XRD of cooled samples did not detect any oxides because of the structurally disordered nature of the oxides. After being cooled, Comm-IN718 showed undesirable oxides like iron oxides in an inhomogeneous crystalline oxide layer. For SLM-IN718 the continuous unbroken oxide layer on the cooled SLM-IN718 sample imparted more effective protection of the alloy.

原文English
文章編號151037
期刊Applied Surface Science
569
DOIs
出版狀態Published - 2021 12月 15

All Science Journal Classification (ASJC) codes

  • 一般化學
  • 凝聚態物理學
  • 一般物理與天文學
  • 表面和介面
  • 表面、塗料和薄膜

指紋

深入研究「In-situ and ex-situ comparison of oxidation of Inconel 718 manufactured by selective laser melting and conventional methods up to 650 °C」主題。共同形成了獨特的指紋。

引用此