Indium-tin-oxide metal-insulator-semiconductor GaN ultraviolet photodetectors using liquid-phase-deposition oxide

Gow Huei Yang, Jun Dar Hwang, Chih Hsueh Lan, Chien Mao Chan, Hone Zem Chen, Shoou Jinn Chang

研究成果: Article同行評審

11 引文 斯高帕斯(Scopus)

摘要

A low-cost and reliable SiO2 insulating layer was successfully deposited onto GaN by liquid-phase deposition (LPD) using supersaturated H 2SiF6 and H3BP3 solutions. The interface-trap density, Dit, was estimated to be 1.2 × 10 12 cm-2 eV-1 for the as-grown, not annealed LPD-SiO2 layers. It was found that the leakage current density was 2.06 × 10-5 A/cm2 at a negative bias of 10 V for the as-grown Al/20nm LPD-SiO2/GaN metal-insulator-semiconductor (MIS) capacitors. It was also found that the LPD-SiO2 layer could be used to suppress the dark current of nitride-based photodetectors. A large photocurrent to dark-current contrast ratio higher than four orders of magnitude and a maximum responsivity of 0.65 A/W were observed from the fabricated indium-tin-oxide (ITO)/LPD-SiO2/GaN MIS UV photodetectors. These results could be explained by defect-assisted tunneling.

原文English
頁(從 - 到)5119-5121
頁數3
期刊Japanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
46
發行號8 A
DOIs
出版狀態Published - 2007 八月 6

All Science Journal Classification (ASJC) codes

  • Engineering(all)
  • Physics and Astronomy(all)

指紋 深入研究「Indium-tin-oxide metal-insulator-semiconductor GaN ultraviolet photodetectors using liquid-phase-deposition oxide」主題。共同形成了獨特的指紋。

引用此