Investigation of CuO -doped NKN ceramics with high mechanical quality factor synthesized by a B-site oxide precursor method

Song Ling Yang, Cheng Che Tsai, Yi Cheng Liou, Cheng Shong Hong, Bing-Jing Li, Sheng-Yuan Chu

研究成果: Article

20 引文 斯高帕斯(Scopus)

摘要

In this study, composition of (Na 0.5K 0.5)NbO 3 + x mol% CuO ceramics (NKNCx, where x = 0-1 mol%) were separately prepared using the B-site oxide precursor method (BO method) and the conventional mixed oxide method (MO method). The diffracted angles of the NKNCx ceramics decreased as the concentrations of CuO dopants increased, because Nb 5+ ions were replaced by Cu 2+ ions, leading to the formation of oxygen vacancies. The microstructures of NKNCx ceramics prepared using the BO method were more homogeneous microstructures than that of ceramics prepared using the MO method. The mechanical quality factor (Q m) and dielectric constant (ε 33 T0) of NKNCx ceramics prepared using the BO method were therefore by 21% and 25% better, respectively. The activation energy and internal bias field were measured and calculated to confirm the presence of oxygen vacancies. A low activation energy corresponds to a high Q m value. NKN ceramics with 0.75 mol% CuO doping prepared using the BO method had an activation energy and internal bias field of 0.95 eV and 3.5 kV/cm, respectively, at x = 0.75 mol%. The bulk density, k p, Q m, ε 33 T0, and dielectric loss of NKNCx ceramics with this composition were 4.488 g/cm 3, 41.5%, 2100, 280, and 0.15%, respectively.

原文English
頁(從 - 到)1011-1017
頁數7
期刊Journal of the American Ceramic Society
95
發行號3
DOIs
出版狀態Published - 2012 三月 1

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

指紋 深入研究「Investigation of CuO -doped NKN ceramics with high mechanical quality factor synthesized by a B-site oxide precursor method」主題。共同形成了獨特的指紋。

  • 引用此