Iron oxide synthesis using a continuous hydrothermal and solvothermal system

Ming Tsai Liang, Shih Han Wang, Yu Lun Chang, Hsing I. Hsiang, Huang Jhe Huang, Meng Huan Tsai, Wen Cheng Juan, Shih Fu Lu

研究成果: Article同行評審

35 引文 斯高帕斯(Scopus)


Iron oxide synthesis via a continuous hydrothermal and solvothermal reaction were studied. In the hydrothermal synthesis, fine α-Fe2O3 (hematite) particles were obtained at 250-420 °C and 30 MPa. The α-Fe2O3 crystals were grown in sub-critical water via a dissolution and precipitation process. The growth of α-Fe2O3 crystals in supercritical water was suppressed due to the rather low solvent power of water. Crystalline Fe3O4 was obtained as the temperature was raised above the supercritical state in the solvothermal preparation. Isopropanol (IPA) was oxidized in acetone which provided a reducing atmosphere. Acetone molecule adsorption onto the Fe3O4 particle surface inhibited crystallite growth.

頁(從 - 到)1131-1135
期刊Ceramics International
出版狀態Published - 2010 4月

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 陶瓷和複合材料
  • 製程化學與技術
  • 表面、塗料和薄膜
  • 材料化學


深入研究「Iron oxide synthesis using a continuous hydrothermal and solvothermal system」主題。共同形成了獨特的指紋。