Kinetic and thermodynamic studies for adsorptive removal of Sr2+ using waste iron oxide

Chia Hsun Liu, Yu Jen Shih, Yao Hui Huang, Chun Ping Huang

研究成果: Article同行評審

22 引文 斯高帕斯(Scopus)

摘要

An iron oxide, BT1, recovered from a real fluidized-bed Fenton reactor, was studied to determine its effectiveness in the adsorptive removal of strontium ions (Sr2+) from water. Millimeter-scale BT1 (0.2-0.5mm) mostly consisted of a poorly crystallized goethite phase (α-FeOOH), with a specific surface area of 185m2/g. Batch jar-testing experiments were conducted at an initial Sr2+ level of 10ppm to determine the effect of pH, the adsorption isotherms, the desorption process, and the kinetics of adsorption. The effectiveness of BT1 as an adsorbent for the removal of Sr2+ depended strongly on pH; at an equilibrium pH of 10.5, 5g BT1 removed almost 100% of Sr2+. Sr2+ was desorbed by a solution of nitric acid at pH 3 with a relatively low rate, and the recycled BT1 maintained its high adsorption efficiency after at least three adsorption-desorption tests. The isotherms were accurately described using both Langmuir and Freundlich models, and the maximum adsorption capacity was found to be 38.46mg/g. The thermodynamic parameters revealed the endothermic and spontaneous nature of the adsorption process at 20-45°C. Kinetic studies revealed that the adsorption of Sr2+ ions on BT1 was a second-order reaction.

原文English
頁(從 - 到)914-920
頁數7
期刊Journal of the Taiwan Institute of Chemical Engineers
45
發行號3
DOIs
出版狀態Published - 2014 五月

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 化學工程 (全部)

指紋

深入研究「Kinetic and thermodynamic studies for adsorptive removal of Sr<sup>2+</sup> using waste iron oxide」主題。共同形成了獨特的指紋。

引用此