Kinetics and mechanism of oxygen reduction at hydrous oxide film-covered platinum electrode in alkaline solution

Chia Chin Chang, Ten Chin Wen

研究成果: Article同行評審

9 引文 斯高帕斯(Scopus)

摘要

This study uses rotating ring-disk electrode (RRDE) and linear sweep voltammetry (LSV) to characterize oxygen reduction kinetics in alkaline solution on platinum electrodes with various thickness of hydrous oxide (oxyhydroxy) film. Oxyhydroxy films are created on Pt electrodes by pretreatment in 1.0 mol dm-3 KOH at a constant voltage. The pretreatment voltage ranges from -1.2 to 1.0 V and is increased stepwise before each new experimental run to produce seven discreet films. LSV plots show oxyhydroxy film thickness strongly inhibits oxygen reduction and is inversely proportional to RRDE oxygen reduction current ID for LSV voltages ED from -0.1 to -0.46 V, but this trend reverses at ED more negative than -0.46 V so that the worst-performing electrode becomes the best. However, this improvement disappears at around -0.8 V, suggesting this change involves a negatively charged ion, possibly embedded into the metal in the top few atomic layers either interstitially or substitutionally. The 1.0 V-pretreated electrode in the ED range from -0.46 to -0.9 V of highest oxygen reduction current also exhibits the lowest hydrogen peroxide production, with zero H2O2 produced at -0.6 V, indicating the brief presence of the oxyhydroxy film on the Pt surface has strong lingering effects. The post-oxyhydroxy Pt surface is very different than the native Pt for oxygen reduction pathway and efficiency. Reaction order with respect to oxygen is close to 1. The rate constants of the direct O2 to H2O electroreduction reaction are increased with decreasing the potential from -0.2 to -0.6 V, but the O2 to H2O2 electroreduction is contrary to this expectation. The rate constants of H2O2 decomposition on the oxyhydroxy film-covered Pt electrode are near constant around 1 × 10-4 cm s-1 at ED > -0.5 V.

原文English
頁(從 - 到)623-629
頁數7
期刊Electrochimica Acta
52
發行號2
DOIs
出版狀態Published - 2006 10月 25

All Science Journal Classification (ASJC) codes

  • 一般化學工程
  • 電化學

指紋

深入研究「Kinetics and mechanism of oxygen reduction at hydrous oxide film-covered platinum electrode in alkaline solution」主題。共同形成了獨特的指紋。

引用此