Liquid phase sintering and microwave dielectric properties of NdAlO3 ceramics

Cheng Liang Huang, Yao Chung Chen

研究成果: Article同行評審

10 引文 斯高帕斯(Scopus)

摘要

The effects of CuO addition on the microstructures and microwave dielectric properties of NdAlO3 ceramics were investigated. CuO was selected as a liquid-phase-sintering aid to lower the sintering temperature of NdAlO3 ceramics. With CuO addition, the sintering temperature of NdAlO3 can be effectively reduced from 1650°C to 1410-1430°C. The crystalline phase exhibited no phase differences at a low addition level while Nd4Al2O9 and NdAl11O18 were presented as second phases at the addition level higher than 0.5 wt%. The quality factors Q × f were strongly dependent upon the CuO concentration. The Q × f value of 63000 GHz was obtained at 1410-1430°C with 0.25 wt% CuO. For all levels of CuO concentration, the relative dielectric constants were not significantly different and ranged from 21.5 to 22.6. The temperature coefficients varied from -30 ppm/°C to -45 ppm/°C. Results of X-ray diffraction analysis and scanning electron microscopy are also presented.

原文English
頁(從 - 到)1459-1464
頁數6
期刊Japanese Journal of Applied Physics
41
發行號3 A
DOIs
出版狀態Published - 2002 3月

All Science Journal Classification (ASJC) codes

  • 一般工程
  • 一般物理與天文學

指紋

深入研究「Liquid phase sintering and microwave dielectric properties of NdAlO3 ceramics」主題。共同形成了獨特的指紋。

引用此