Low dielectric loss ceramics in the Mg4Nb2O9-ZnAl2O4-TiO2 ternary system

Yu Chuan Wu, Hsiao Ting Tseng, Chi Shiung Hsi, Jari Juuti, Hsing I. Hsiang

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

This study used a traditional solid-state reaction method to prepare a series of composite ceramics in the 0.7Mg4Nb2O9-(0.3-x)ZnAl2O4-xTiO2 ternary system. Crystalline phases and microstructure of Mg4Nb2O9-ZnAl2O4-TiO2 dielectric ceramic composites were investigated and correlated with the relevant dielectric properties. It was observed that the addition of Ti4+ substituted Nb5+ in the Mg4Nb2O9 structure, which promoted the decomposition of Mg4Nb2O9 to form the second phase, Mg5Nb4O15, during sintering. The synergistic effect of ZnAl2O4-TiO2 co-doping promoted the Mg4Nb2O9 ceramic densification. The sample (0.7Mg4Nb2O9-(0.3-x)ZnAl2O4-xTiO2) with x = 0.15−0.2 exhibited dielectric constants of 13–14, larger than those of ZnAl2O4, Mg4Nb2O9 and Mg5Nb4O15, due to the NbO6 octahedra distortion resulting from the substitution of Al3+/Ti4+ for Nb5+ in Mg4Nb2O9 and Mg5Nb4O15. The long-range order of the NbO6 octahedra was enhanced by co-doping ZnAl2O4 and TiO2, thereby enhancing the Qxf value. A dielectric constant of 13.1, Qxf value of 366,000 GHz and a τf of −60.8 ppm/°C were obtained from 1300 °C sintered 0.7Mg4Nb2O9-0.15ZnAl2O4-0.15TiO2. These results show that 0.7Mg4Nb2O9-0.15 ZnAl2O4-0.15TiO2 ceramic is a good candidate for microwave electronic device applications.

原文English
頁(從 - 到)448-452
頁數5
期刊Journal of the European Ceramic Society
42
發行號2
DOIs
出版狀態Published - 2022 2月

All Science Journal Classification (ASJC) codes

  • 陶瓷和複合材料
  • 材料化學

指紋

深入研究「Low dielectric loss ceramics in the Mg4Nb2O9-ZnAl2O4-TiO2 ternary system」主題。共同形成了獨特的指紋。

引用此