Low-Pressure Vapor-Assisted Solution Process for Thiocyanate-Based Pseudohalide Perovskite Solar Cells

Yu Hsien Chiang, Hsin Min Cheng, Ming Hsien Li, Tzung Fang Guo, Peter Chen

研究成果: Article同行評審

30 引文 斯高帕斯(Scopus)

摘要

In this report, we fabricated thiocyanate-based perovskite solar cells with low-pressure vapor-assisted solution process (LP-VASP) method. Photovoltaic performances are evaluated with detailed materials characterizations. Scanning electron microscopy images show that SCN-based perovskite films fabricated using LP-VASP have long-range uniform morphology and large grain sizes up to 1 μm. The XRD and Raman spectra were employed to observe the characteristic peaks for both SCN-based and pure CH3NH3PbI3 perovskite. We observed that the Pb(SCN)2 film transformed to PbI2 before the formation of perovskite film. X-ray photoemission spectra (XPS) show that only a small amount of S remained in the film. Using LP-VASP method, we fabricated SCN-based perovskite solar cells and achieved a power conversion efficiency of 12.72 %. It is worth noting that the price of Pb(SCN)2 is only 4 % of PbI2. These results demonstrate that pseudo-halide perovskites are promising materials for fabricating low-cost perovskite solar cells.

原文English
頁(從 - 到)2620-2627
頁數8
期刊ChemSusChem
9
發行號18
DOIs
出版狀態Published - 2016 9月 22

All Science Journal Classification (ASJC) codes

  • 環境化學
  • 一般化學工程
  • 一般材料科學
  • 一般能源

指紋

深入研究「Low-Pressure Vapor-Assisted Solution Process for Thiocyanate-Based Pseudohalide Perovskite Solar Cells」主題。共同形成了獨特的指紋。

引用此