Low-temperature resistivity and microstructure of reactive magnetron co-sputtered Ta-Si-N thin films

Chen-Kuei Chung, A. Nautiyal, T. S. Chen

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

The low-temperature electrical property of composite tantalum silicon nitride (Ta-Si-N) thin films deposited at low and high nitrogen flow ratios (FN2%) has been investigated. The microstructure and morphology of both quasi-amorphous Ta-Si-N films were characterized by a grazing incident x-ray diffractometer, scanning electron microscope and atomic force microscope, which could influence the electrical resistivity of Ta-Si-N at low temperatures of 10-300 K. The film deposited at low FN2% had a lower resistivity because of low N content compared with that at high FN2%. The resistivity of Ta-Si-N at low FN2% distinctly decreased with increasing temperature at 10-300 K while that at high FN2% had a steep drop at 70-120 K. The transport mechanism of Ta-Si-N resistivity at low temperatures was discussed by the weak localization model. The film deposited at high FN2% showed crossover from 2D localization to 3D localization while that at low FN2% exhibited only the 3D localization. Both samples showed that electron-phonon scattering was the dominant scattering mechanism in both 2D and 3D weak localization effects.

原文English
文章編號295406
期刊Journal of Physics D: Applied Physics
43
發行號29
DOIs
出版狀態Published - 2010 七月 16

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 凝聚態物理學
  • 聲學與超音波
  • 表面、塗料和薄膜

指紋

深入研究「Low-temperature resistivity and microstructure of reactive magnetron co-sputtered Ta-Si-N thin films」主題。共同形成了獨特的指紋。

引用此