Low temperature sintering and microwave dielectric properties of 0.5LaAlO3-0.5SrTiO3 ceramics using copper oxide additions

Cheng Shing Hsu, Cheng Liang Huang, Jing Fang Tseng, Cheng Chi You

研究成果: Article同行評審

10 引文 斯高帕斯(Scopus)


The microwave dielectric properties and the microstructures of 0.5LaAlO3-0.5SrTiO3 ceramics with CuO addition prepared with conventional solid-state route have been investigated. Doping with CuO (up to 1 wt.%) can effectively promote the densification and remain comparable dielectric properties of 0.5LaAlO3-0.5SrTiO3 ceramics. It is found that 0.5LaAlO3-0.5SrTiO3 ceramics can be sintered at 1400 °C due to the sintering aid effect resulted from CuO as addition observed by scanning electron microscopy. The dielectric constant as well as the Q × f value decreases with increasing CuO content. At 1460 °C, 0.5LaAlO3-0.5SrTiO3 ceramics with 0.25 wt.% CuO addition possess a dielectric constant (εr) of 35.2, a Q × f value of 24000 (at 8 GHz) and a temperature coefficient of resonant frequency (τf) of -13.5 ppm/°C.

頁(從 - 到)2067-2073
期刊Ceramics International
出版狀態Published - 2004 十一月 15

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Process Chemistry and Technology
  • Surfaces, Coatings and Films
  • Materials Chemistry

指紋 深入研究「Low temperature sintering and microwave dielectric properties of 0.5LaAlO<sub>3</sub>-0.5SrTiO<sub>3</sub> ceramics using copper oxide additions」主題。共同形成了獨特的指紋。