Mechanisms of degradation of polymer composites by galvanic reactions between metals and carbon fiber

Eamor Woo, J. S. Chen, C. S. Carter

研究成果: Article同行評審

9 引文 斯高帕斯(Scopus)

摘要

Toughened and untoughened epoxy and BMI carbon fiber reinforced composites were evaluated in terms of their matrix chemical stability in galvanic reactions between metals and composites. It has been known that the presence of moisture and salts and contact between unprotected metals and BMI carbon fiber composition constitute prerequisite conditions for composite degradation. This study has further demonstarated that these conditions were necessary, but not sufficient. It was found that the OH species generated by galvanic reactions had to be concentrated in localized spots to induce composite degradation at a significant rate. A mechanism was proposed to elucidate how degradation took place under those necessary conditions with the aid of localized aggregation of the OH species. Additionally, thoughening of BMI composite matrix resins resulted in poorer resistance to degradation by galvanic reactions. On the other hand, none of the eposy composites (toughened or untoughened) exhibited any degradation due to galvanic reactions at room temperature, nor did they degrade in a concentrated caustic NaOH solution (pH = 14,82°C) that simulated a highly accelerated galvanie reaction.

原文English
頁(從 - 到)395-401
頁數7
期刊Polymer Composites
14
發行號5
DOIs
出版狀態Published - 1993 一月 1

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Chemistry(all)
  • Polymers and Plastics
  • Materials Chemistry

指紋 深入研究「Mechanisms of degradation of polymer composites by galvanic reactions between metals and carbon fiber」主題。共同形成了獨特的指紋。

引用此