Melt synthesis of oxide red phosphors La2WO6:Eu 3+

Tadashi Ishigaki, Nobuhiro Matsushita, Masahiro Yoshimura, Kazuyoshi Uematsu, Kenji Toda, Mineo Sato

研究成果: Conference article同行評審

7 引文 斯高帕斯(Scopus)


To synthesize various complex oxide materials and their solid solutions, we have applied a novel "melt-synthesis technique" rather than conventional solid-state reaction techniques. The synthesis of well-crystalline multi-component phosphor materials is sometimes difficult using conventional solid-state reaction techniques because the reaction rates are slow as a result of slow mutual diffusion among solid-state species, thereby creating an inhomogeneous product. However, the melt reaction is rapid and homogeneous as it proceeds because of a solution reaction with fast diffusion. Red-phosphor La2WO6:Eu3+ samples with 25 mol% Eu 3+ were prepared in a short time using melt synthesis. Red emission was observed at 618 nm typical for the Eu3+ center. Melt-synthesized samples exhibited much higher emission intensities than those obtained for the sample prepared using a solid-state reaction.

頁(從 - 到)587-601
期刊Physics Procedia
出版狀態Published - 2009 8月
事件2008 International Conference on Luminescence and Optical Spectroscopy of Condensed Matter, ICL'08 - Lyon, France
持續時間: 2008 7月 72008 7月 11

All Science Journal Classification (ASJC) codes

  • 物理與天文學 (全部)


深入研究「Melt synthesis of oxide red phosphors La2WO6:Eu 3+」主題。共同形成了獨特的指紋。