Metalorganic vapor phase epitaxy growth of m-plane GaN using LiAlO 2 substrates

An Ting Cheng, Yan Kuin Su, Wei-Chi Lai, Ying Zhi Chen

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

The crystalline, surface, and optical properties of the m-plane GaN layer grown on the LiAlO2 (LAO) substrate by metalorganic vapor phase epitaxy (MOVPE) were demonstrated. The low temperature growth of the GaN buffer layer, performed in the nitrogen ambient, could lead to the smooth surface morphology. Because of the small lattice mismatch between GaN and the LAO substrate, the low-density line-shaped defects, possibly originated from stacking faults, were observed. In addition, high phase purity of the m-plane GaN epilayer was shown in the high resolution X-ray diffraction (HRXRD) spectrum. The different behavior was found for donor-bound exciton (D 0X) and defect-related transitions, characterized by the temperature-dependent photoluminescence (PL) measurement. These results suggest that the nitridation process and low temperature growth of the GaN buffer layer under nitrogen ambient could be suitable for realizing smooth and high phase purity m-plane GaN on LAO substrates.

原文English
頁(從 - 到)3074-3076
頁數3
期刊Japanese Journal of Applied Physics
47
發行號4 PART 2
DOIs
出版狀態Published - 2008 四月 25

All Science Journal Classification (ASJC) codes

  • 工程 (全部)
  • 物理與天文學 (全部)

指紋

深入研究「Metalorganic vapor phase epitaxy growth of m-plane GaN using LiAlO <sub>2</sub> substrates」主題。共同形成了獨特的指紋。

引用此