Microstructural characteristics of PTA-overlayed NbC on pure Ti

Fei Yi Hung, Zao You Yan, Li Hui Chen, Truan Sheng Lui

研究成果: Article同行評審

16 引文 斯高帕斯(Scopus)

摘要

This study uses the technique of PTA (plasma transferred arc) to overlay NbC reinforcing particles on the surface of commercially pure Ti in order to investigate the microstructural features of the overlayer and the interface between the overlayer and base metal by changing the overlaying current. The results indicate that the matrix phase of the overlayer was α-Ti containing about 10 at.% Nb and 1 at.% C. NbC and precipitated TiC produced by dissolved NbC reacted with Ti dispersed in the matrix. The microstructure of the cross-section of the overlayer (from surface to base metal), which was composed of α-Ti, can be separated into three layers: an upper overlayer with TiC, a middle overlayer with TiC and NbC, and a lower overlayer (interfacial layer and heat affected zone, HAZ). Due to solidification beginning at the interface and the effect of dilution, the TiC in the interfacial layer was finer. Owing to faster solidification under low-current conditions, the TiC particles were finer than under high-current conditions. Also, dendritic TiC under a low-current in the upper overlayer was also finer than under a high-current. Meanwhile, TiC precipitate that resulted from heterogeneous nucleation and Gibbs' free energy was also found around NbC. This NbC diffusion layer between TiC and NbC may have been βNb2C phase.

原文English
頁(從 - 到)6881-6887
頁數7
期刊Surface and Coatings Technology
200
發行號24
DOIs
出版狀態Published - 2006 八月 1

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

指紋 深入研究「Microstructural characteristics of PTA-overlayed NbC on pure Ti」主題。共同形成了獨特的指紋。

引用此