Microstructure and magnetism of Co-doped PbPdO2 films with different grain sizes

F. L. Tang, J. Liu, C. Mei, S. Y. Huang, T. T. Song, H. L. Su, M. K. Lee, Y. C. Wu, J. C.A. Huang

研究成果: Article同行評審

10 引文 斯高帕斯(Scopus)

摘要

Single-phase Co-doped PbPdO2 films with grain sizes ranging from 30 nm to 120 nm were synthesized using a sol-gel spin-coating method. The doped Co ions exhibit a mixed state of 2+ and 3+, which is caused by the existence of Pb vacancies and the low electronegativity of Co. Ferromagnetism, paramagnetism, antiferromagnetism and a charge ordering state were observed in all of the Co-doped PbPdO2 films. Additionally, the charge ordering signal determined by the surface state of the nanograins is gradually weakened with decreasing grain size. The carrier-mediated mechanism bridged to the bound magnetic polaron model was used to explain the coexistence of the ferromagnetism, paramagnetism and antiferromagnetism. For the ferromagnetism, the tendency of the saturation magnetization to increase with temperature was found in all the Co-doped PbPdO2 films with a nanograin structure. This abnormal magnetic behavior is believed to be one of the peculiar features of spin gapless semiconductors.

原文English
頁(從 - 到)37522-37529
頁數8
期刊RSC Advances
6
發行號44
DOIs
出版狀態Published - 2016 一月 1

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Chemical Engineering(all)

指紋 深入研究「Microstructure and magnetism of Co-doped PbPdO<sub>2</sub> films with different grain sizes」主題。共同形成了獨特的指紋。

引用此