Microstructure and magnetism of sol-gel synthesized Co-doped PbPdO2 nanograin film

T. T. Song, F. L. Tang, H. L. Su, P. Y. Chuang, J. Liu, C. Mei, S. Y. Huang, M. K. Lee, J. C.A. Huang, Y. C. Wu

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)

摘要

The single-phase body-centered-orthorhombic-structured Co-doped PbPdO2 thin film was obtained using the sol-gel spin-coating method and an oxidation treatment. The film had a nanograin microstructure with an average grain size of about 56 nm and a thickness of about 150 nm. The adoption of a moderate calcination temperature of 650°C was found to be very important for preparing the single-phase-PbPdO2-based film with a high crystalline quality. The magnetic studies exhibited that the ferromagnetism and the paramagnetism coexist within the formed Co-doped PbPdO2 film and the ferromagnetism can be maintained above room temperature. The saturation magnetization of the ferromagnetism increasing with the temperature, as the peculiar characteristic of the spin gapless semiconductor, was found within the film. The investigation on the film's X-ray absorption near-edge structure revealed that the ferromagnetism of the Co-doped PbPdO2 is intrinsic.

原文English
頁(從 - 到)37-41
頁數5
期刊Journal of Magnetism and Magnetic Materials
407
DOIs
出版狀態Published - 2016 六月 1

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 凝聚態物理學

指紋

深入研究「Microstructure and magnetism of sol-gel synthesized Co-doped PbPdO<sub>2</sub> nanograin film」主題。共同形成了獨特的指紋。

引用此