Microstructures and surface step-induced antiphase boundaries in epitaxial ferroelectric Ba 0.6Sr 0.4TiO 3 thin film on MgO

J. C. Jiang, Y. Lin, C. L. Chen, C. W. Chu, E. I. Meletis

研究成果: Article同行評審

58 引文 斯高帕斯(Scopus)

摘要

Ba 0.6Sr 0.4TiO 3 thin films were epitaxially grown on (001) MgO substrates using pulsed laser ablation. Cross-sectional and plan-view transmission electron microscopy have been employed to study the microstructures and the interface behavior of the as-grown thin films. The 110-nm-thick Ba 0.6Sr 0.4TiO 3 thin films have a flat surface and sharp interface. The entire thin film has a single-crystal cubic structure with an interface relationship of (001) Ba 0.6Sr 0.4TiO 3//(001) MgO and 〈100〉 Ba 0.6Sr 0.4TiO 3//〈100〉 MgO with respect to the substrate. The 6.4% lattice mismatch between Ba 0.6Sr 0.4TiO 3 and MgO was completely released at the interface by forming equally spaced misfit dislocations with a distance of ∼3.2 nm. High-resolution transmission electron microscopy investigation shows that the initial grown layer of the film is the TiO 2 monolayer. The growth models of "substrate surface-terrace induced defects" for perovskite on a rock-salt system have been developed to understand the as-grown features where the conservative and nonconservative antiphase boundaries can be formed.

原文English
頁(從 - 到)3188-3192
頁數5
期刊Journal of Applied Physics
91
發行號5
DOIs
出版狀態Published - 2002 2月 15

All Science Journal Classification (ASJC) codes

  • 物理與天文學 (全部)

指紋

深入研究「Microstructures and surface step-induced antiphase boundaries in epitaxial ferroelectric Ba 0.6Sr 0.4TiO 3 thin film on MgO」主題。共同形成了獨特的指紋。

引用此