Microstructures of Cu-rich Amalgams after Corrosion

J. H.C. Lin; G. W. Marshall; S. J. Marshall

doi:10.1177/00220345830620020401

Microstructures of Cu-rich Amalgams after Corrosion

J. H.C. Lin, G. W. Marshall, S. J. Marshall

產學創新總中心

研究成果: Article › 同行評審

36 引文斯高帕斯（Scopus）

摘要

In vitro corrosion of Cu-rich amalgams resulted in selective attack of the η’ phase. Copper was removed, and SnO₂ products were found in pores and along matrix grain boundaries. The corrosion process greatly accelerated the γ₁→β₁ transformation.

原文	English
頁（從 - 到）	112-115
頁數	4
期刊	Journal of Dental Research
卷	62
發行號	2
DOIs	https://doi.org/10.1177/00220345830620020401
出版狀態	Published - 1983 2月

All Science Journal Classification (ASJC) codes

牙科 (全部)

存取文件

10.1177/00220345830620020401

其它文件與鏈接

Link to publication in Scopus

引用此

@article{44041a50a2284d99bd086af6d1b7533c,

title = "Microstructures of Cu-rich Amalgams after Corrosion",

abstract = "In vitro corrosion of Cu-rich amalgams resulted in selective attack of the η{\textquoteright} phase. Copper was removed, and SnO2 products were found in pores and along matrix grain boundaries. The corrosion process greatly accelerated the γ1→β1 transformation.",

author = "Lin, {J. H.C.} and Marshall, {G. W.} and Marshall, {S. J.}",

year = "1983",

month = feb,

doi = "10.1177/00220345830620020401",

language = "English",

volume = "62",

pages = "112--115",

journal = "Journal of Dental Research",

issn = "0022-0345",

publisher = "SAGE Publications Inc.",

number = "2",

}

TY - JOUR

T1 - Microstructures of Cu-rich Amalgams after Corrosion

AU - Lin, J. H.C.

AU - Marshall, G. W.

AU - Marshall, S. J.

PY - 1983/2

Y1 - 1983/2

N2 - In vitro corrosion of Cu-rich amalgams resulted in selective attack of the η’ phase. Copper was removed, and SnO2 products were found in pores and along matrix grain boundaries. The corrosion process greatly accelerated the γ1→β1 transformation.

AB - In vitro corrosion of Cu-rich amalgams resulted in selective attack of the η’ phase. Copper was removed, and SnO2 products were found in pores and along matrix grain boundaries. The corrosion process greatly accelerated the γ1→β1 transformation.

UR - http://www.scopus.com/inward/record.url?scp=0020638550&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0020638550&partnerID=8YFLogxK

U2 - 10.1177/00220345830620020401

DO - 10.1177/00220345830620020401

M3 - Article

C2 - 6571862

AN - SCOPUS:0020638550

VL - 62

SP - 112

EP - 115

JO - Journal of Dental Research

JF - Journal of Dental Research

SN - 0022-0345

IS - 2

ER -

Microstructures of Cu-rich Amalgams after Corrosion

摘要

All Science Journal Classification (ASJC) codes

存取文件

其它文件與鏈接

指紋

引用此