Microwave dielectric properties and microstructure of 0.85MgTiO 3-0.15Ca0.6la0.8/3TiO3 dielectric ceramics with added sintering aids

Yuan Bin Chen, Cheng Liang Huang, Chen Weng Lon, Chih Hung Wei, Yu Ping Hsieh, Yi Hong Huang

研究成果: Article同行評審

摘要

The effects of additive sintering aids on the microstructures and microwave dielectric properties of 0.85MgTiO3-0.15Ca0.6La 0.8/3TiO3 ceramics were investigated. CuO was selected as a liquid phase sintering aid to lower the sintering temperature of 0.85MgTiO3-0.15Ca0.6La0.8/3TiO3 ceramics. With added CuO, the densification temperature of 0.85MgTiO 3-0.15Ca0.6La0.8/3TiO3 can be effectively reduced from 1450 to 1160-1300°C. Low-level doping of CuO (0.5-5 wt %) significantly improves the density and dielectric properties of 0.85MgTiO3-0.15Ca0.6La0.8/3TiO3 ceramics. The quality factor Q × f was strongly dependent upon the amount of additives, Q × f values of 60000 and 20000 GHz could be obtained at 1160-1300°C with 0.5 and 5 wt % CuO added, respectively. Over all ranges of addition, the relative dielectric constants differed significantly and ranged from 23.2 to 26.1. The temperature coefficient varied from 0 to -3.7 ppm/°C.

原文English
頁(從 - 到)5086-5091
頁數6
期刊Japanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
44
發行號7 A
DOIs
出版狀態Published - 2005 七月 8

All Science Journal Classification (ASJC) codes

  • 工程 (全部)
  • 物理與天文學 (全部)

指紋

深入研究「Microwave dielectric properties and microstructure of 0.85MgTiO <sub>3</sub>-0.15Ca<sub>0.6</sub>la<sub>0.8/3</sub>TiO<sub>3</sub> dielectric ceramics with added sintering aids」主題。共同形成了獨特的指紋。

引用此