TY - JOUR
T1 - Microwave dielectric properties and microstructures of CuO-modified (1 - X)(Mg0.95Co0.05)TiO3-xCaTiO3 ceramic system
AU - Huang, Cheng Liang
AU - Pan, Chung Long
AU - Hsu, Jui Feng
PY - 2004/8
Y1 - 2004/8
N2 - The effects of CuO additives on the microstructures and the microwave dielectric properties of (1 - x)(Mg0.95Co0.05)TiO 3-xCaTiO3 ceramics were investigated. The CuO additives can effectively reduce the sintering temperature of the ceramics to as low as 1175°C. With x = 0.08, at 1275°C, the 0.92(Mg0.95Co 0.05)TiO3-0.08CaTiO3 ceramic possesses excellent microwave dielectric properties: a dielectric constant εr of 22.1, a Q × f value of 86400 GHz (at 7 GHz) and a τf value of 5.4 ppm/°C. Sintered ceramic samples were characterized by using X-ray diffraction pattern and SEM. Dielectric constants (εr) are not significantly affected by various additives and range from 20 to 23. By properly adjusting the x of (1 - x)(Mg 0.95Co0.05)TiO3-xCaTiO3 ceramics, small temperature coefficients (<±3ppm/°C) of resonant frequency (τf) are obtained for 0.93(Mg0.95Co 0.05)TiO3-0.07CaTiO3 with 0.25 wt% CuO additives.
AB - The effects of CuO additives on the microstructures and the microwave dielectric properties of (1 - x)(Mg0.95Co0.05)TiO 3-xCaTiO3 ceramics were investigated. The CuO additives can effectively reduce the sintering temperature of the ceramics to as low as 1175°C. With x = 0.08, at 1275°C, the 0.92(Mg0.95Co 0.05)TiO3-0.08CaTiO3 ceramic possesses excellent microwave dielectric properties: a dielectric constant εr of 22.1, a Q × f value of 86400 GHz (at 7 GHz) and a τf value of 5.4 ppm/°C. Sintered ceramic samples were characterized by using X-ray diffraction pattern and SEM. Dielectric constants (εr) are not significantly affected by various additives and range from 20 to 23. By properly adjusting the x of (1 - x)(Mg 0.95Co0.05)TiO3-xCaTiO3 ceramics, small temperature coefficients (<±3ppm/°C) of resonant frequency (τf) are obtained for 0.93(Mg0.95Co 0.05)TiO3-0.07CaTiO3 with 0.25 wt% CuO additives.
UR - http://www.scopus.com/inward/record.url?scp=6344237293&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=6344237293&partnerID=8YFLogxK
U2 - 10.1143/JJAP.43.5384
DO - 10.1143/JJAP.43.5384
M3 - Article
AN - SCOPUS:6344237293
SN - 0021-4922
VL - 43
SP - 5384
EP - 5387
JO - Japanese Journal of Applied Physics
JF - Japanese Journal of Applied Physics
IS - 8 A
ER -