Microwave dielectric properties of B2O3 doped LaAlO3 ceramics at low sintering temperature

Cheng Shing Hsu, Cheng Liang Huang, Kuo Hau Chiang

研究成果: Article同行評審

10 引文 斯高帕斯(Scopus)

摘要

The microwave dielectric properties and the microstructures of LaAlO3 ceramics with B2O3 additions (0.25-1 wt%) prepared with conventional solid-state route have been investigated. Doping with B2O3 (up to 0.5 wt%) can effectively promote the densification of LaAlO3 ceramics. It is found that LaAlO3 ceramics can be sintered at 1400°C due to the liquid phase effect of B2O3 addition. The Q × f value as well as the dielectric constant decreases at higher B2O3 doping level (1 wt%) due to the increase of boundary phases. At 1460°C, LaAlO3 ceramics with 0.5 wt% B2O3 addition possesses a dielectric constant (εr) of 22.9, a Q × f value of 44700 (at 9 GHz) and a temperature coefficients of resonant frequency (τf) of -36 ppm/°C. The B2O3-doped LaAlO3 ceramics can find applications in microwave devices requiring low sintering temperature.

原文English
頁(從 - 到)3495-3500
頁數6
期刊Journal of Materials Science
38
發行號16
DOIs
出版狀態Published - 2003 8月 15

All Science Journal Classification (ASJC) codes

  • 一般材料科學
  • 材料力學
  • 機械工業

指紋

深入研究「Microwave dielectric properties of B2O3 doped LaAlO3 ceramics at low sintering temperature」主題。共同形成了獨特的指紋。

引用此