Model With Experimental Evidences for the Morphology of Binary Blends of a Thermosetting Polycyanate with Thermoplastics

Eamor Woo, Chean C. Su, J. F. Kuo, James C. Seferis

研究成果: Article同行評審

35 引文 斯高帕斯(Scopus)

摘要

A proposed mechanical model based on our modification of the conventional Takayanagi model was successfully used to describe the dynamic mechanical modulus data of binary blends of a high-temperature thermosetting polycyanate (Bisphenol E dicyanate) with thermoplastics (polysulfone or poly(ether imide)). The model parameters were found to quantitatively agree well with the physical compositions of the phases in the blends. The modeling results suggested interesting shifts in the phase continuity of the blends as a function of the thermoplastic contents. At low thermoplastic contents (10% and below), the blends exhibited a simple continuous-dispersed phase morphology, with the continuous polycyanate phase surrounding the dispersed phase. As the thermoplastic contents increased (20 vol % and above), a notable change in the phase composition and morphology was observed in the dispersed domains, and a continuous thermoplastic phase started to form, while the polycyanate continuous phase retreated rapidly. The findings from the modeling were also further experimentally substantiated by optical and electron microscopy observations.

原文English
頁(從 - 到)5291-5296
頁數6
期刊Macromolecules
27
發行號19
DOIs
出版狀態Published - 1994 九月 1

All Science Journal Classification (ASJC) codes

  • Organic Chemistry
  • Polymers and Plastics
  • Inorganic Chemistry
  • Materials Chemistry

指紋 深入研究「Model With Experimental Evidences for the Morphology of Binary Blends of a Thermosetting Polycyanate with Thermoplastics」主題。共同形成了獨特的指紋。

引用此