Molecular dynamical investigation on dislocation near twist-grain boundary of Ni under compression

Jun Liang Chen, Jin Yuan Hsieh, Jee Gong Chang, Hong Chang Lin, Hsing Jung Chiang, Huang Kai Huang, Chi Chuan Hwang

研究成果: Article同行評審

7 引文 斯高帕斯(Scopus)

摘要

The dislocations and the strength of a nickel bicrystal are investigated in present study. There are three kinds of crystalline orientations of the nickel bicrystal, namely (100), (110), and (111). Misfit dislocations are presented on the interface between two nickel grains when a compression process is utilized on the bicrystal. The misfit dislocations on a Ni(100) interface form a square-latticed network and those on a Ni(111) form a triangle-latticed network. When a large twist angle is applied to the Ni bicrystal, the square- and triangle-latticed unit of the misfit dislocation networks will shrink or even disappear. Thus, a plane defects distribute over the interface. If the bicrystal is compressed further, dislocations within each grain are developed from the defects on the interface between grains. The configuration of the dislocations within grains is more regular when the applied twist angle is smaller. A Ni(111) bicrystal owns the largest amount of maximal stress no matter what the twist angle is. Those of a Ni(110) bicrystal is the second and of a Ni(100) bicrystal is the smallest.

原文English
文章編號094315
期刊Journal of Applied Physics
110
發行號9
DOIs
出版狀態Published - 2011 11月 1

All Science Journal Classification (ASJC) codes

  • 一般物理與天文學

指紋

深入研究「Molecular dynamical investigation on dislocation near twist-grain boundary of Ni under compression」主題。共同形成了獨特的指紋。

引用此