Morphology and glass transition behavior of polycarbonate-phenoxy system: Effects of trans-reactions in domain interface regions

E. M. Woo, S. N. Yau

研究成果: Article同行評審

7 引文 斯高帕斯(Scopus)

摘要

Effects of trans reactions on the morphology, glass transition, and phase behavior in a classical blend system of a poly(hydroxyl ether bisphenol-A) (phenoxy) with bisphenol-A polycarbonate (PC) were investigated by differential scanning calorimetry (DSC) and optical microscopy. Although two Tgs were observed in the as-prepared PC/phenoxy blends, an apparently single, but broadened. Tg was found in the blends after heating at high temperatures, typically 200-250°C for short times. The optical microscopy results indicated that same scales of heterogeneity did exist in post-heated PC/phenoxy blends as well as unheated blends. Explanations were provided. After heating-induced interchange reactions (- OH and carbonate), randomly linked polymer chains might form at the numerous interfaces of the mutually occluded/included micro-domains. The majority of the chains in the micro-domains are forced to relax in coordinated motion modes after heating, thus showing a single Tg-. A mechanism of trans reactions in interfacial regions was briefly discussed in supplement to earlier reports in the literature.

原文English
頁(從 - 到)97-103
頁數7
期刊Journal of Polymer Science, Part A: Polymer Chemistry
35
發行號1
DOIs
出版狀態Published - 1997 一月 15

All Science Journal Classification (ASJC) codes

  • Polymers and Plastics
  • Organic Chemistry
  • Materials Chemistry

指紋 深入研究「Morphology and glass transition behavior of polycarbonate-phenoxy system: Effects of trans-reactions in domain interface regions」主題。共同形成了獨特的指紋。

引用此