Nitridation of Titanium and Zirconium Powders Mixed with Ammonium Chloride under High Temperature-High Pressure Ammonia

Masahiro Yoshimura, Kazuo Suzuki, Shigeyuki Somiya

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

Titanium and zirconium powders did not yield nitrides effectively by the treatment in pressurized ammonia of 1 MPa and above, at 700°C for 3 h. The addition of NH4CI was effective for the nitridation of Ti and Zr. Reactions of titanium powder (99.1% up) mixed with 10 wt% (9.2 mol%) ammonium chloride have been studied at 300–700oC under 0.1 or 1 MPa NH3 (initial pressure) for 3 h. Ti and NH4CI did not react at 300°C, but formed TiHi.924at 400°C, and then TiHi.924changed into TiN above 500°C. When the sample of Ti-10 wt% NH4CI was heated at 300–600°C under 0.4 MPa Ar gas for 3 h, TiHi.924was produced at 400°C and above, but TiN was not produced. When the sample of Zr-10 mol% (6 wt%) NH4CI was heated under 0.1 or 1 MPa NH3, ZrN was formed above 600°C through the formation of ZrH and above 400°C. A small amount of ß-ZrNCl was also produced at 700°C under the same conditions.

原文English
頁(從 - 到)78-84
頁數7
期刊journal of the japan society of powder and powder metallurgy
34
發行號2
DOIs
出版狀態Published - 1987

All Science Journal Classification (ASJC) codes

  • 機械工業
  • 工業與製造工程
  • 金屬和合金
  • 材料化學

指紋

深入研究「Nitridation of Titanium and Zirconium Powders Mixed with Ammonium Chloride under High Temperature-High Pressure Ammonia」主題。共同形成了獨特的指紋。

引用此