Observation of a second-order distortion in Nd3Co4Sn13

C. W. Wang, C. N. Kuo, H. F. Liu, C. S. Lue, L. M. Wang, J. W. Lin, K. C. Rule, J. S. Gardner

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

In this paper we report the resistivity and neutron scattering experiments on Nd3Co4Sn13. These results indicate that Nd3Co4Sn13 undergoes a structural distortion from a high-temperature primitive cubic unit cell to an I-centered superstructure and a concomitant doubling of the lattice constant. The P m -3 n structure of Yb3Rh4Sn13 describes well the neutron powder diffraction pattern collected at room temperature, but failed to fit the low–temperature profiles due to the presence of (h/2 k/2 l)-type diffraction peaks. Single crystal elastic neutron scattering performed in the [h h l] scattering plane shows the lattice distortion with mean field character at 124 (2) K as the temperature is lowered. Besides, three I-centered space groups are excluded by the single crystal diffraction work, including I -4 3 d symmetry which is observed in other R3T4Sn13 compounds.

原文English
頁(從 - 到)12-15
頁數4
期刊Physica B: Condensed Matter
551
DOIs
出版狀態Published - 2018 十二月 15

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering

指紋 深入研究「Observation of a second-order distortion in Nd<sub>3</sub>Co<sub>4</sub>Sn<sub>13</sub>」主題。共同形成了獨特的指紋。

引用此