Optically transparent of n-ZnO/p-NiO heterojunction for ultraviolet photodetector application

Shu Yi Tsai, Min Hsiung Hon, Yang Ming Lu

研究成果: Conference contribution

3 引文 斯高帕斯(Scopus)

摘要

Transparent p-n heterojunction diodes consisting of n-type ZnO and p-type NiO thin films were prepared on glass substrates by r.f. magnetron sputtering. The structural and optical properties of the n-ZnO/p-NiO heterojunction were characterized by X-ray diffraction (XRD), UV-visible spectroscopy, Hall measurement, and I-V photocurrent measurements. The XRD shows that ZnO films are highly crystalline in nature with preferred orientation along the (0 0 2) orientation. The optical transmittances of ZnO and NiO films are 87% and 80%, respectively. The current-voltage curve of the heterojunction demonstrates obvious rectifying diode behavior in a dark environment. The lowest of leakage current is 7.73×10-8 A/cm2 for n-ZnO/p-NiO heterojunction diode. Upon UV irradiation, it was found that the detector current was increased by more than one order of magnitude. It was also found that the corresponding time constant for turn-on transient was τon = 27.9 ms while that for turn-off transient was τoff= 62.8 ms.

原文English
主出版物標題Functional and Electronic Materials
發行者Trans Tech Publications Ltd
頁面711-715
頁數5
ISBN(列印)9783037851692
DOIs
出版狀態Published - 2011

出版系列

名字Materials Science Forum
687
ISSN(列印)0255-5476
ISSN(電子)1662-9752

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 凝聚態物理學
  • 材料力學
  • 機械工業

指紋

深入研究「Optically transparent of n-ZnO/p-NiO heterojunction for ultraviolet photodetector application」主題。共同形成了獨特的指紋。

引用此