Passivation of titanium in molybdate-containing sulphuric acid solution

Tzyy Ping Cheng, Ju Tung Lee, Wen-Ta Tsai

研究成果: Article

39 引文 斯高帕斯(Scopus)

摘要

The effect of molybdate ions on the passivation reaction of commercial pure (CP) Ti in sulphuric acid solution was studied by conducting an immersion test, measuring dc polarization curves and electrochemical impedance spectroscopy (EIS). It is found that the addition of molybdate in boiling sulphuric acid with concentrations higher than 10-3 M could greatly reduce the corrosion rate to a negligible value. dc Polarization curves showed that the passivation behaviour was strongly affected by the solution temperature as well as the concentration of molybdate ion present in the sulphuric acid. The passive film resistance (Rpf) determined by EIS was found to increase with the externally applied anodic potential and/or with the molybdate ion concentration. The increase of Rpf is mainly attributed to the thickening process of oxide film at more noble potentials.

原文English
頁(從 - 到)2069-2076
頁數8
期刊Electrochimica Acta
36
發行號14
DOIs
出版狀態Published - 1991 一月 1

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)
  • Electrochemistry

指紋 深入研究「Passivation of titanium in molybdate-containing sulphuric acid solution」主題。共同形成了獨特的指紋。

  • 引用此