Performance improvement of perovskite solar cells using electron and hole transport layers

Guan Syun Chen, Yi Ching Chen, Ching Ting Lee, Hsin Ying Lee

研究成果: Article

7 引文 斯高帕斯(Scopus)


In this study, various electron and hole transport structures were created in perovskite solar cells to ameliorate the problem of carrier mobility balance. Balanced electron and hole mobilities could reduce carrier recombination probability in the cells to improve their performance. The space-charge-limited current (SCLC) method was used to calculate the electron and hole mobilities of perovskite devices with various electron transport layers (ETLs) and hole transport layers (HTLs). Compared with perovskite devices with [6,6]-phenyl-C-61-butyric acid methyl ester (PC60BM) single ETL and poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) single HTL, the current density and power-conversion efficiency of perovskite solar cells with [6,6]-phenyl-C-71-butyric acid methyl ester/pristine fullerenes (PC70BM/C70) dual ETLs and PEDOT:PSS/poly[4,8-bis[(2-ethylhexyl)oxy]benzo[1,2-b:4,5-b′]dithiophene-2,6-diyl][3-fluoro-2-[(2-ethylhexyl)carbonyl]thieno[3,4-b]-thiophenediyl] (PTB7) dual HTLs increased from 18.22 to 24.11 mA/cm2 and 7.07% to 14.11%, respectively. Compared with the carrier mobility balance ratio (μhe) of 0.35 of perovskite solar cells with PC60BM single ETL and PEDOT:PSS single HTL, perovskite solar cells with dual ETLs and dual HTLs showed a μhe of 0.90, which led to the performance improvement of the cells.

頁(從 - 到)897-900
期刊Solar Energy
出版狀態Published - 2018 十一月 1

All Science Journal Classification (ASJC) codes

  • Renewable Energy, Sustainability and the Environment
  • Materials Science(all)

指紋 深入研究「Performance improvement of perovskite solar cells using electron and hole transport layers」主題。共同形成了獨特的指紋。