A series of aliphatic polyesters having CH2/COO ratios from 2 to 14 in their repeat units were blended with a copolymer of vinylidene chloride containing 13.5% by weight of vinyl chloride. Blends of polyesters having CH2/COO < 4 did not form completely miscible amorphous phases, whereas polyesters having CH2/COO ≥ 4 did form completely homogeneous amorphous phases for all temperatures below the decomposition point except for the polyester with CH2/COO = 14 which showed reversible phase separation on heating, i.e., lower critical solution temperature behavior. Interaction parameters were estimated by melting point depression and by analog calorimetry. The behavior reported here is qualitatively similar to that reported earlier for blends of aliphatic polyesters with poly(vinyl chloride), polyepichlorohydrin, polycarbonate, styrene–allyl alcohol copolymers, and the hydroxy ether of bisphenol A.