Phase evolution and microwave dielectric properties of TiO 2-modified (Mg0.95Co0.05)2TiO 4 ceramics

Cheng Liang Huang, Jhih Yong Chen

研究成果: Article

3 引文 斯高帕斯(Scopus)

摘要

Phase evolution and microwave dielectric properties of (1 - x)(Mg 0.95Co0.05)2TiO4-xTiO2 (x = 0-1) ceramics prepared by the conventional mixed oxide route have been investigated. Increasing the TiO2 content would lead to a main phase transformation from (Mg0.95Co0.05)2TiO 4 to (Mg0.95Co0.05)TiO3, (Mg 0.95Co0.05)Ti2O5 and then TiO 2. Not only did the TiO2 addition compensate the τf, it also lowered the sintering temperature of specimen. A huge drop of Q × f occurs at a 40-60 mol% TiO2 addition was attributed to the formation of (Mg0.95Co0.05)Ti 2O5 phase. Specimen with x = 0.78 can possess an excellent combination of microwave dielectric properties: εr ∼ 24.77, Q × f ∼ 38,500 GHz and τf ∼ -1.3 ppm/°C.

原文English
頁(從 - 到)6273-6275
頁數3
期刊Journal of Alloys and Compounds
509
發行號21
DOIs
出版狀態Published - 2011 五月 26

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

指紋 深入研究「Phase evolution and microwave dielectric properties of TiO <sub>2</sub>-modified (Mg<sub>0.95</sub>Co<sub>0.05</sub>)<sub>2</sub>TiO <sub>4</sub> ceramics」主題。共同形成了獨特的指紋。