Phase formation of zinc titanate precursor powders prepared by a hydrothermal process in various ph environments

Cheng Li Wang, Weng Sing Hwang, Hsueh Liang Chu, Horng Huey Ko, Chi Shiung Hsi, Wang Long Li, Kuo Ming Chang, Moo Chin Wang

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

For the precursor, powders were calcined at 773 K (500 °C) for 1 hour. The anatase TiO2 and ZnO appear as the predominant and minor phases, respectively, when the precursor powders are obtained at pH 5. The phases of Zn2Ti3O8, anatase TiO2, and ZnO coexist for the precursor powders obtained at pH 7. In addition, the Zn 2Ti3O8 and ZnO are the predominant and minor phases, respectively, for the precursor powders obtained at pH 9.

原文English
頁(從 - 到)2689-2698
頁數10
期刊Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
45
發行號6
DOIs
出版狀態Published - 2014 六月

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys

指紋 深入研究「Phase formation of zinc titanate precursor powders prepared by a hydrothermal process in various ph environments」主題。共同形成了獨特的指紋。

引用此