Photoluminescence of nano-scaled YAG:Ce phosphor powders

In Gann Chen, Yulin Chen, Chii Shyang Hwang, F. S. Juang, S. J. Chang, Y. K. Su, G. O. Mueller, R. Mueller-Mach

研究成果: Conference article同行評審

1 引文 斯高帕斯(Scopus)

摘要

Four series of YAG:Ce phosphor powders were synthesized by solid state, co-precipitation, and sol-gel (with two different growth inhibitors, HMDS and PAA respectively) methods, which results in the average particle sizes of 800, 56, 43, and 32 nm respectively. All the nano-scale YAG powders were heat treated below 1000_. Both TEM and XRD results of these nano-scale YAG powders show high degree of crystalline structure. Photoluminescence (PL) characterization shows that the nano-scale YAG phosphor powders emit a higher intensity of luminescence than that of sub-micro sized samples. The effect of different Ce doping level on the PL of (Y3-xCex)Al5O12 shows a maximum at x ∼ 0.01. The Commission International de I'Eclairage (CIE) chromaticity coordinates were determined and show different trends of shifts in the resulting PL spectra. Systematic study of the processing parameters characterized by DTA/TGA, XRD, FTIR, and BET will be discussed in detail in the report.

原文English
頁(從 - 到)89-95
頁數7
期刊Materials Research Society Symposium - Proceedings
727
DOIs
出版狀態Published - 2002
事件Nanostructured Interfaces - San Francisco, CA, United States
持續時間: 2002 四月 22002 四月 4

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 凝聚態物理學
  • 材料力學
  • 機械工業

指紋

深入研究「Photoluminescence of nano-scaled YAG:Ce phosphor powders」主題。共同形成了獨特的指紋。

引用此