Polymerized Complex Synthesis of the Modulation-free (Bi, Pb)2 Sr2(Ca, R)Cu2O8+d (R: Rare Earth=Y)

Masato Kakihana, Minoru Osada, Masatomo Yashima, Masahiro Yoshimura, Toshiya Abiko, Sugitani Yoshinori, Hiromasa Mazaki, Hiroshi Yasuoka

研究成果: Article同行評審

摘要

High-purity ceramic samples of the modulation-free Bi2-xPbxSr2Ca1-yYyCu2Oz with a wide range of composition (x=(l+y)/2±0.2, 0.25≤y≤0.8) have been prepared by the polymerized complex method. The method is based on the formation of a polymer complex which is obtained through polyesterfication between metal citrate complexes and ethylene glycol. This method yielded almost homogeneous x=0.8 materials with Y compositions of y=0.2, 0.6 and 0.8 through relatively short sintering periods of 32 hours. The corresponding X-ray diffraction and Raman scattering analyses have shown that the materials are virtually of single phase with only minor traces of Sr2.5Bi0.5Pb3Ca2CuOz (< 1 %). The lattice parameters a and b increase, while the c-axis value decreases with increasing Y content, y. Complex magnetic susceptibility measurements have confirmed the presence of a single bulk Bi2212 phase. For Bi1.2Pb0.8Sr2Ca0.8Y0.2Cu2Oz, the onset temperature of superconducting transition Tc was 89.5 K and the transition width (10-90 %) of full diamagnetism was 6.4 K for the measuring field of 100 mOe. The variation of Tc with Y content in the modulation-free Bi2212 phase was similar with that observed in the modulated Bi2Sr2Ca1-yYyCu2Oz.

原文English
頁(從 - 到)735-740
頁數6
期刊journal of the japan society of powder and powder metallurgy
42
發行號6
DOIs
出版狀態Published - 1995

All Science Journal Classification (ASJC) codes

  • Mechanical Engineering
  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

指紋 深入研究「Polymerized Complex Synthesis of the Modulation-free (Bi, Pb)<sub>2</sub> Sr<sub>2</sub>(Ca, R)Cu<sub>2</sub>O<sub>8+d</sub> (R: Rare Earth=Y)」主題。共同形成了獨特的指紋。

引用此