Polyvinylbutyral assisted synthesis and characterization of chalcopyrite quaternary semiconductor Cu(InxGa1-x)Se2 nanofibers by electrospinning route

Lin Jer Chen, Jiunn Der Liao, Yu Ju Chuang, Yaw Shyan Fu

研究成果: Article同行評審

5 引文 斯高帕斯(Scopus)


Chalcopyrite quaternary semiconductor Cu (InxGa1-x) Se2 nanocrystals were successfully prepared via a relatively simple electrospinning route and characterized using X-ray powder diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TGA) and transmission electron microscopy (TEM). Semiconductor Cu(InxGa 1-x)Se2 nanofibers were obtained for PVB/Cu(In xGa1-x)Se2 precursor at an applied voltage of 20 kV after annealing treatment at 400 °C for 6 h. The optical property of Cu (InxGa1-x) Se2 nanocrystals was also recorded by means of UV-vis absorption spectroscopy. We also report the first electrospinning synthesis of uniform chalcopyrite crystals Cu (In xGa1-x)Se2 nanofibers and demonstrate can be used to create simple thin film solar cells, with our first cells exhibiting an efficiency of 1.96% under AM1.5 illumination.

頁(從 - 到)116-121
出版狀態Published - 2011 一月 7

All Science Journal Classification (ASJC) codes

  • Organic Chemistry
  • Polymers and Plastics
  • Materials Chemistry

指紋 深入研究「Polyvinylbutyral assisted synthesis and characterization of chalcopyrite quaternary semiconductor Cu(In<sub>x</sub>Ga<sub>1-x</sub>)Se<sub>2</sub> nanofibers by electrospinning route」主題。共同形成了獨特的指紋。