Post-annealing effect upon optical properties of electron beam evaporated molybdenum oxide thin films

Shih Yuan Lin, Ying Chung Chen, Chih Ming Wang, Po Tsung Hsieh, Shun Chou Shih

研究成果: Article同行評審

59 引文 斯高帕斯(Scopus)

摘要

Molybdenum oxide (MoO 3 ) thin films were deposited by electron beam evaporation. The chemical composition, microstructure, optical and electrical properties of MoO 3 thin films depend on the annealing temperature and ambient atmosphere. X-ray diffraction (XRD) shows that crystalline MoO 3 films can be obtained at various post-annealing temperatures from 200 to 500 °C in N 2 and O 2 . X-ray photoelectron spectroscopy (XPS) results reveal that the O-1s emission peak was shifted slightly toward lower binding energies as the annealing temperature in N 2 was increased. The oxygen vacancies and conductivity of MoO 3 film increased with the annealing temperature. However, when the MoO 3 films were annealed in an atmosphere of O 2 , the optical transmission, the O/Mo ratio and the photon energy increased with the annealing temperature. The results differ from those for films annealed in a N 2 atmosphere.

原文English
頁(從 - 到)3868-3874
頁數7
期刊Applied Surface Science
255
發行號6
DOIs
出版狀態Published - 2009 一月 1

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 凝聚態物理學
  • 物理與天文學 (全部)
  • 表面和介面
  • 表面、塗料和薄膜

指紋

深入研究「Post-annealing effect upon optical properties of electron beam evaporated molybdenum oxide thin films」主題。共同形成了獨特的指紋。

引用此