Preparation and characteristics of ferrite catalysts for reduction of CO2

Chii Shyang Hwang, Neng Cheng Wang

研究成果: Article同行評審

70 引文 斯高帕斯(Scopus)

摘要

To reduce CO2 gas, high specific surface and high activity of (MnxZn1-x)Fe2O4 and (Mn xNi1-x)Fe2O4 nano-sized powders were synthesized by the hydrothermal process and used as catalysts. Effects of the composition of synthesized ferrites, the activated time of the catalysts, and the flow rate of carbon dioxide on the decomposition of carbon dioxide were investigated. The crystalline Mn-Zn ferrite catalysts with 21-29nm nano-scale particle size and 73-143m2g-1 specific surface area were synthesized by hydrothermal process at 150°C for 2h. The (Mn 0.33Zn0.67)Fe2O4 catalyst shows the best CO2 decomposition performance after reduction in H2 at 300°C for 4h. The crystalline Mn-Ni ferrite catalysts with 18-24nm nano-scale particle size and 107-153m2g-1 specific surface area were synthesized by hydrothermal process at 140°C for 2h. The (Mn 0.67Ni0.33)Fe2O4 catalyst shows the best CO2 decomposition performance after reduction in H2 300°C for 2h. The Mn-Zn ferrite showed a better CO2 decomposition efficiency than that of Mn-Ni catalyst with the same Mn content.

原文English
頁(從 - 到)258-263
頁數6
期刊Materials Chemistry and Physics
88
發行號2-3
DOIs
出版狀態Published - 2004 十二月 15

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 凝聚態物理學

指紋

深入研究「Preparation and characteristics of ferrite catalysts for reduction of CO<sub>2</sub>」主題。共同形成了獨特的指紋。

引用此