Preparation and properties of a high temperature, flexible and colorless ITO coated polyimide substrate

研究成果: Article同行評審

47 引文 斯高帕斯(Scopus)

摘要

A new high temperature, flexible and colorless indium-tin-oxide (ITO) coated plastic substrate has been prepared from a thermally stable, high glass transition temperature (Tg) and colorless polyimide film. The polyimide was synthesized from 3,3′-diaminodiphenylsulfone (3,3′-DDS) and 4,4′-(hexafluoroisopropylidene) diphthalic anhydride (6FDA) monomers. Its heat distortion temperature was 278 °C. The ITO was deposited on the polyimide film using the magnetron-sputtering process. After annealing at 250 °C under nitrogen for 1 h, the resistivity of the ITO film was 4.0 × 10-4 Ω cm, and its transmittance was 83.5%. Scanning electron microscope (SEM) and X-ray diffraction (XRD) were used to observe the surface and morphology of the ITO film. UV-visible spectroscopy and the four-probe method were used to study their optical and electrical properties. The high performance ITO-plastic substrate can be used in the next generation flat panel displays.

原文English
頁(從 - 到)3368-3373
頁數6
期刊European Polymer Journal
43
發行號8
DOIs
出版狀態Published - 2007 八月

All Science Journal Classification (ASJC) codes

  • 物理與天文學 (全部)
  • 聚合物和塑料
  • 有機化學
  • 材料化學

指紋

深入研究「Preparation and properties of a high temperature, flexible and colorless ITO coated polyimide substrate」主題。共同形成了獨特的指紋。

引用此