PREPARATION AND PROPERTIES OF PEROVSKITE-TYPE COMPOUND Sr2CrWO6.

Masahiro Yoshimura, Akira Okada, Tetsuro Nakamura

研究成果: Conference article

摘要

A single phase of Sr//2CrWO//6 was synthesized by the solid state reaction of oxide mixtures at 1400 degree C in the atmosphere of H//2 plus H//2O. The lattice constant was 7. 818 plus or minus 0. 002 angstroms with the space group Fm3m. Superstructure lines in the X-ray diffraction pattern showed that Cr-ion and W-ion were ordered partially ( approximately equals 66%) in this compound. This compound was ferrimagnetic and the Curie temperature was 448 K. The electrical conductivity was 1. 2 multiplied by 10** minus **4 (ohm multiplied by (times) cm)** minus **1 at 300 K.

原文English
頁(從 - 到)53-58
頁數6
期刊Telcom Report (English Edition)
出版狀態Published - 1978 一月 1

All Science Journal Classification (ASJC) codes

  • Hardware and Architecture
  • Electrical and Electronic Engineering

指紋 深入研究「PREPARATION AND PROPERTIES OF PEROVSKITE-TYPE COMPOUND Sr<sub>2</sub>CrWO<sub>6</sub>.」主題。共同形成了獨特的指紋。

  • 引用此