Preparation of electrospun luminescent polyimide/europium nanofibers by simultaneous in situ sol-gel and imidization processes

Si Cheng, Xiaofei Li, Sibai Xie, Yun Chen, Li Juan Fan

研究成果: Article同行評審

17 引文 斯高帕斯(Scopus)

摘要

Luminescent polyimide (PI)/europium nanofibers have been successfully prepared by electrospinning combined with an in situ sol-gel technique. The possible reaction mechanism of the simultaneous imidization of polyamide acid and gelation of europium phase was analyzed by thermogravimetric analysis (TG) and differential scanning calorimetry (DSC). The results showed that chemical coupling and noncovalent interaction existed between the polymer and the europium which formed during the preparative process. Fourier-transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM), and scanning electronic spectroscopy (SEM) studies also indicated the successful incorporation of europium into PI matrix and various morphologies could be achieved by controlling the calcination temperature and the europium content. Nanofibers with necklace-like structures were obtained after calcination under high temperatures. These PI/europium nanofibers were further demonstrated to have strong fluorescence emission. The intensity ratio for the PI/europium nanofibers, labeled as (5D07F2)/(5D07F1), which is well known as the asymmetry parameter, was lower than that in pure Eu2O3 powder, indicating that there were highly symmetric coordination spheres around europium in the nanofibers.

原文English
頁(從 - 到)92-99
頁數8
期刊Journal of Colloid And Interface Science
356
發行號1
DOIs
出版狀態Published - 2011 四月 1

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Biomaterials
  • Surfaces, Coatings and Films
  • Colloid and Surface Chemistry

指紋 深入研究「Preparation of electrospun luminescent polyimide/europium nanofibers by simultaneous in situ sol-gel and imidization processes」主題。共同形成了獨特的指紋。

引用此