Preparation of low water-sorption lightweight aggregates from harbor sediment added with waste glass

Yu Ling Wei, Chang Yuan Lin, Kuan Wei Ko, H. Paul Wang

研究成果: Article同行評審

40 引文 斯高帕斯(Scopus)

摘要

A harbor sediment is successfully recycled at 1150. °C as low water-absorption lightweight aggregate via addition of waste glass powder. Sodium content in the waste glass is responsible for the formation of low-viscosity viscous phases during firing process to encapsulate the gases generated for bloating pellet samples. Water sorption capacity of the lightweight products can be considerably reduced from 5.6% to 1.5% with the addition of waste glass powder. Low water-absorption property of lightweight products is beneficial for preparing lightweight concrete because the water required for curing the cement would not be seized by lightweight aggregate filler, thus preventing the failure of long-term concrete strength.

原文English
頁(從 - 到)135-140
頁數6
期刊Marine Pollution Bulletin
63
發行號5-12
DOIs
出版狀態Published - 2011

All Science Journal Classification (ASJC) codes

  • Oceanography
  • Aquatic Science
  • Pollution

指紋 深入研究「Preparation of low water-sorption lightweight aggregates from harbor sediment added with waste glass」主題。共同形成了獨特的指紋。

引用此