Preparation of mesoporous cerium oxide templated by tri-block copolymer for solid oxide fuel cell

I. M. Hung; H. P. Wang; W. H. Lai; K. Z. Fung; M. H. Hon

doi:10.1016/j.electacta.2004.03.059

Preparation of mesoporous cerium oxide templated by tri-block copolymer for solid oxide fuel cell

I. M. Hung, H. P. Wang, W. H. Lai, K. Z. Fung, M. H. Hon

研究成果: Article › 同行評審

33 引文斯高帕斯（Scopus）

摘要

Mesoporous structured CeO₂ with high specific surface area was synthesized at ambient temperature in this study. The synthesis of this material was accomplished using a tri-block copolymer as the organic supermolecular template and the cerium nitrate hexahydrate as the inorganic precursor. X-ray diffraction, nitrogen adsorption and desorption isotherms and transmission electron microscopy have been used to characterize the mesoporous structure. The nitrogen adsorption and desorption isotherms analysis indicates that the average pore size is 3.5 and 3.4nm and the specific surface area is 155 and 103 m²/g for the samples calcined at 523 and 723 K, respectively.

原文	English
頁（從 - 到）	745-748
頁數	4
期刊	Electrochimica Acta
卷	50
發行號	2-3
DOIs	https://doi.org/10.1016/j.electacta.2004.03.059
出版狀態	Published - 2004 11月 30

All Science Journal Classification (ASJC) codes

化學工程 (全部)
電化學

存取文件

10.1016/j.electacta.2004.03.059

其它文件與鏈接

引用此

@article{76e737cd3e574943bf93d6506bba5f2c,

title = "Preparation of mesoporous cerium oxide templated by tri-block copolymer for solid oxide fuel cell",

abstract = "Mesoporous structured CeO2 with high specific surface area was synthesized at ambient temperature in this study. The synthesis of this material was accomplished using a tri-block copolymer as the organic supermolecular template and the cerium nitrate hexahydrate as the inorganic precursor. X-ray diffraction, nitrogen adsorption and desorption isotherms and transmission electron microscopy have been used to characterize the mesoporous structure. The nitrogen adsorption and desorption isotherms analysis indicates that the average pore size is 3.5 and 3.4nm and the specific surface area is 155 and 103 m2/g for the samples calcined at 523 and 723 K, respectively.",

author = "Hung, {I. M.} and Wang, {H. P.} and Lai, {W. H.} and Fung, {K. Z.} and Hon, {M. H.}",

note = "Funding Information: This work is sponsored by National Science Council (NSC) in Taiwan, under the grant No. NSC 92-2120-M-006-003",

year = "2004",

month = nov,

day = "30",

doi = "10.1016/j.electacta.2004.03.059",

language = "English",

volume = "50",

pages = "745--748",

journal = "Electrochimica Acta",

issn = "0013-4686",

publisher = "Elsevier Limited",

number = "2-3",

}

TY - JOUR

T1 - Preparation of mesoporous cerium oxide templated by tri-block copolymer for solid oxide fuel cell

AU - Hung, I. M.

AU - Wang, H. P.

AU - Lai, W. H.

AU - Fung, K. Z.

AU - Hon, M. H.

N1 - Funding Information: This work is sponsored by National Science Council (NSC) in Taiwan, under the grant No. NSC 92-2120-M-006-003

PY - 2004/11/30

Y1 - 2004/11/30

N2 - Mesoporous structured CeO2 with high specific surface area was synthesized at ambient temperature in this study. The synthesis of this material was accomplished using a tri-block copolymer as the organic supermolecular template and the cerium nitrate hexahydrate as the inorganic precursor. X-ray diffraction, nitrogen adsorption and desorption isotherms and transmission electron microscopy have been used to characterize the mesoporous structure. The nitrogen adsorption and desorption isotherms analysis indicates that the average pore size is 3.5 and 3.4nm and the specific surface area is 155 and 103 m2/g for the samples calcined at 523 and 723 K, respectively.

AB - Mesoporous structured CeO2 with high specific surface area was synthesized at ambient temperature in this study. The synthesis of this material was accomplished using a tri-block copolymer as the organic supermolecular template and the cerium nitrate hexahydrate as the inorganic precursor. X-ray diffraction, nitrogen adsorption and desorption isotherms and transmission electron microscopy have been used to characterize the mesoporous structure. The nitrogen adsorption and desorption isotherms analysis indicates that the average pore size is 3.5 and 3.4nm and the specific surface area is 155 and 103 m2/g for the samples calcined at 523 and 723 K, respectively.

UR - http://www.scopus.com/inward/record.url?scp=9344243571&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=9344243571&partnerID=8YFLogxK

U2 - 10.1016/j.electacta.2004.03.059

DO - 10.1016/j.electacta.2004.03.059

M3 - Article

AN - SCOPUS:9344243571

SN - 0013-4686

VL - 50

SP - 745

EP - 748

JO - Electrochimica Acta

JF - Electrochimica Acta

IS - 2-3

ER -

Preparation of mesoporous cerium oxide templated by tri-block copolymer for solid oxide fuel cell

摘要

All Science Journal Classification (ASJC) codes

存取文件

其它文件與鏈接

指紋

引用此