Preparation of ordered mesoporous carbons containing well-dispersed and highly alloying Pt-Co bimetallic nanoparticles toward methanol-resistant oxygen reduction reaction

Shou Heng Liu, Feng Sheng Zheng, Jyun Ren Wu

研究成果: Article同行評審

48 引文 斯高帕斯(Scopus)

摘要

A simple route is described for the synthesis of well-dispersed and highly alloying PtCo bifunctional nanoparticles supported on ordered mesoporous carbons (Pt100-xCox/OMC) by the simultaneous pyrolysis of carbon and metal precursors in a mesoporous silica as the hard template. A variety of different spectroscopic and analytical techniques was used to thoroughly characterize the Pt100-xCox/OMC samples. By X-ray diffraction, N2 adsorption/desorption isotherms and transmission electron microscopy, it was found that Pt100-xCox/OMC possessed well-dispersed Pt/PtCo nanoparticles (2-3nm) supported on high surface area (~1000m2g-1) and regular pore channels (~2.8nm). Among Pt100-xCox/OMC catalysts, the Pt50Co50/OMC was found to have superior electrocatalytic activity and the tolerance to methanol crossover during oxygen reduction reaction as compared to typical commercial electrocatalysts. This may be attributed to the dispersion and unique nanostructure of highly alloyed PtCo nanoparticles supported on Pt50Co50/OMC evidenced by X-ray absorption spectroscopy.

原文English
頁(從 - 到)81-89
頁數9
期刊Applied Catalysis B: Environmental
108-109
DOIs
出版狀態Published - 2011 十月 11

All Science Journal Classification (ASJC) codes

  • Catalysis
  • Environmental Science(all)
  • Process Chemistry and Technology

指紋 深入研究「Preparation of ordered mesoporous carbons containing well-dispersed and highly alloying Pt-Co bimetallic nanoparticles toward methanol-resistant oxygen reduction reaction」主題。共同形成了獨特的指紋。

引用此