Preparation of Pd/Ti nanostructured electrodes by electrophoretic deposition

C. C. Wang, Dong-Hwang Chen, T. C. Huang

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

A Pd/Ti nanostructured electrode was prepared by means of electrophoretic deposition of monodispersed Pd nanoparticles (11.9nm) in reverse micellar solution, followed by sintering in an atmosphere of Ar/H2(9/1) at 400°c for 2h. Although small Pd agglomerates (c.a. 36nm) were formed, they could be deposited in an ordered manner on a Ti support under the electric field. The electrochemical properties of the sintered Pd/Ti electrodes with various Pd amounts were investigated by means of cyclic voltammetry in 1.0 M NaOH solution. It was observed that the resultant Pd/Ti nanostructured electrodes showed significantly higher electrocatalytic activities and lower hydrogen overpotentials than did the bulk Pd electrodes due to their large specific surface areas. In addition, it was found that the hydrogen overpotential was significantly reduced with a smaller amount of deposited Pd. This could be attributed to the increase of the specific surface area, resulting from reduced sintering.

原文English
頁(從 - 到)289-294
頁數6
期刊Journal of the Chinese Institute of Chemical Engineers
32
發行號4
出版狀態Published - 2001 七月

All Science Journal Classification (ASJC) codes

  • 化學工程 (全部)

指紋

深入研究「Preparation of Pd/Ti nanostructured electrodes by electrophoretic deposition」主題。共同形成了獨特的指紋。

引用此