Processing and mechanical properties of hydroxyapatite reinforced with hydroxyapatite whiskers

Wojciech Suchanek, Masatomo Yashima, Masato Kakihana, Masahiro Yoshimura

研究成果: Article同行評審

110 引文 斯高帕斯(Scopus)

摘要

Hydrothermally synthesized HAp fine crystals/HAp whiskers mixtures have been used for the preparation of HAp/0-30% (whiskers) composites. The composites have been fabricated by pressureless sintering and hot-pressing. The best mechanical properties and the highest densities have been achieved for composites hot pressed at 1000°C (2 h, 30 MPa in flowing Ar). Their density was in the range of 90-97% of the theoretical density. Fracture toughness (K(lc)) of the composites reflected their microstructure and had the value of 1.4 MPa (1/2) (as compared with K(lc) = 1.0 MPam(1/2) for the non-reinforced HAp matrix). Compressive prestressing of the HAp matrix and crack deflection (both derived from the residual stress field) contributed to the increase of fracture toughness. Other toughening mechanisms have not been observed. HAp/HAp (whiskers) composites exhibited improved toughness without degradation of biocompatibility, because the HAp whiskers acted both as a reinforcement and as a biocompatible phase. Problems related to biocompatibility and mechanical properties of available HAp-based composites were also discussed.

原文English
頁(從 - 到)1715-1723
頁數9
期刊Biomaterials
17
發行號17
DOIs
出版狀態Published - 1996 九月

All Science Journal Classification (ASJC) codes

  • Bioengineering
  • Ceramics and Composites
  • Biophysics
  • Biomaterials
  • Mechanics of Materials

指紋 深入研究「Processing and mechanical properties of hydroxyapatite reinforced with hydroxyapatite whiskers」主題。共同形成了獨特的指紋。

引用此