Promotion of piezoelectric properties of lead zirconate titanate ceramics with (Zr,Ti) partially replaced by Nb2O5

Bing Huei Chen, Cheng Liang Huang, Long Wu

研究成果: Article同行評審

22 引文 斯高帕斯(Scopus)

摘要

This study investigated the correlation of sintering effects on piezoelectric properties of Nb modified lead zirconate titanate (PZT) piezoceramics produced by the conventional solid reaction sintering. Samples were prepared at a composition Zr/Ti=53/47, contiguous to a morphotropic phase boundary (MPB) for 1 mol% Nb2O5. Replacement of Ti +4 by Nb+5 in such perovskite type solid solutions was accomplished by the creation of cation vacancies. These created vacancies seemed to facilitate material transport and benefit sintering. Calcined at 850 °C/2 h and sintered at 1250 °C/2 h, the PZT ceramics yielded a minimum value of the mechanical quality factor (Qm) 50, and exhibited a maximum electromechanical coupling factor κp 0.62, in accordance with the relationship between the mechanical quality factor and electromechanical coupling factor. In addition, during the sintering process a piezoelectric charge constant at d33 was found to be of 385 pC/N. It was noted that the fundamental resonance frequency was around 200 kHz, which was suitable for piezoelectric nebulizer (fluid atomizer), ultrasonic cleaning transducer applications.

原文English
頁(從 - 到)2293-2297
頁數5
期刊Solid-State Electronics
48
發行號12
DOIs
出版狀態Published - 2004 十二月 1

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering
  • Materials Chemistry

指紋 深入研究「Promotion of piezoelectric properties of lead zirconate titanate ceramics with (Zr,Ti) partially replaced by Nb<sub>2</sub>O<sub>5</sub>」主題。共同形成了獨特的指紋。

引用此