Properties of CeO2-Al2O3-SiO2 glasses prepared in an atmosphere of nitrogen

S. L. Lin, Chii-Shyang Hwang

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

Properties of (20-30) mol% CeO2-(16-23) mol% Al2O3-(47-62) mol% SiO2 glasses prepared in an atmosphere of N2 have been investigated. Experimental results showed that the glass transformation temperature, dilatometric softening temperature and transmittance in the visible region decrease with increasing ceria content; and that the thermal expansion coefficient and microhardness increase with increasing ceria content. The cerous ions in cerium aluminosilicate glasses exhibited a broad fluorescence spectrum with a large Stoke shift at 450 nm from the excitation spectrum peak of 366 nm. The fluorescence peaks shifted to the shorter wavelength but cutoff wavelength of ultraviolet spectra shifted to the longer wavelength as cerium aluminosilicate glasses were prepared in air instead of in N2 for the specimen of the same composition.

原文English
頁(從 - 到)1209-1213
頁數5
期刊Yogyo Kyokai Shi/Journal of the Ceramic Society of Japan
103
發行號12
出版狀態Published - 1995 十二月 1

All Science Journal Classification (ASJC) codes

  • 工程 (全部)

指紋

深入研究「Properties of CeO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> glasses prepared in an atmosphere of nitrogen」主題。共同形成了獨特的指紋。

引用此